El objetivo del presente trabajo fue evaluar la resistencia al desgaste de seis materiales restauradores estéticos, utilizando como abrasivo una pasta dentífrica a base de bicarbonato de sodio y un dispositivo ad hoc con cepillos dentales, simulando una situación clínica, para considerar su utilización en restauraciones de lesiones cervicales por abrasión. Se confeccionaron 10 probetas (n = 60) de cada material, quedando conformados los siguientes grupos: F (F2000/3M ESPE); A (A110/3M ESPE); DY(Dyract Flow/Dentsply);T (Tetric Ceram/Vivadent); PH (Photac Fil/3M ESPE) y PF (Perma Flo/Ultradent). Se registró la masa inicial para cada espécimen (PI) previamente al ensayo experimental; posteriormente las probetas fueron pesadas nuevamente para determinar la masa final (PF) a los 7, 30 y 60 días. De la diferencia entre los valores registrados (PI/PF), en los diferentes períodos de tiempo, se dedujo la pérdida total de masa para cada material. El mayor desgaste lo presentó el ionómero vítreo híbrido con diferencias significativas con respecto a los otros materiales y sólo a los siete días. Palabras clave: desgaste, materiales estéticos, lesiones cervicales.

SUMMARY

The aim of this study was to assess the wear resistance of six aesthetic restorative materials using a sodium bicarbonate based toothpaste as abrasive material and a specially designed device with toothbrushes, simulating a clinical background, in order to consider their usage in abrasion cervical lesions restorations. 10 specimens for each material (n=60) were prepared, and the following groups were obtained: F (F200013M ESPE); A (Al10/3M ESPE); DV (Dyract Flow/Dentsply); T (Tetric Ceram/Nivadent): PH (Photac Fil/3M ESPE) y PF (PermaFlo/Ultradent). The initial mass (PI) for each specimen was registered prior to the experimental essay. Lately the specimens' weight was once again measured in order to register their final mass (PF) at 7, 30 and 60 days. The total mass loss for each for each material, in all time periods, was obtained as a difference of the registered values (Pl/PF). The greatest wear loss was observed in the hybrid glass ionomer cement, with significant differences regarding the other materials and only at 7 days. Key Words: wear, aesthetic materials, cervical lesions.

| Volver |