CLINICA E PESQUISA ODONTOLOGICA REVISTA DE

Vol. 1 No. 4      ABRIL-JUNHO 2005

ISSN: 1807-5274      UBIC: 295-M

RESUMO

Objetivos:Avaliar a reaçao dos tecidos subcutaneos do rato ao MTA, cimento Portland e cimento Portland branco acrescido de resma epòxica. Devido as similaridades na composiçao entre o MTA e cimento Portland, o cimento Portland branco foi misturado com resma epòxica para obter um material mais consistente, o qual poderia ser de manipulacao mais facil durante os procedimentos clìnicos. Metodologia: O MTA e cimento Portland foram misturados com agua destilada na proporçao de 3:1 (pò/liquido). O cimento Portland branco foi misturado com resma epoxica na mesma proporçao. O material foi colocado em tubos de polietileno e implantados no dorso de ratos Wistar. Tubos vazios foram utilizados como controle. Os animais foram mortos aos 7.30 e 60 dias e amostras da pele contendo os tubos foram removidos e processados para exame histològico. Resultados: aos 7 dias, um tecido granulomatoso foi observado pròximo a extremidade do tubo, caracterizado por linfòcitos, cèlulas gigantes multinucleadas e abundantes macròfagos em torno de uma area necròtica. Aos 30 dias, o tecido em torno do tubo apresentava sinais iniciais de reparo, caracterizado por fibròcitos e fibras colagenas. Detectou-se igualmente um infiltrado inflamatòrio, caracterizado por muitos macròfagos e alguns linfòcitos. Aos 60 dias, um processo avançado de reparo foi observado. Nao houve diferenças estatìsticas entre os grupos de 7 e 60 dias (p>0,05). Entretanto, algumas diferenças foram observadas aos 30 dias. Foram observadas mais areas com tecido granulomatoso e fibròticas no grupo cimento Portland quando comparado com os outros cimentos (p<0,05). Linfòcitos foram observados em nùmero maior no grupo do cimento Portland acrescido de resina epòxica (p<0,05) (Kruskal Wallis). Conclusòes: Os materiais nao foram irritantes na area estudada, principalmente nos maiores tempos che permanència e nao interferiram com o processo natural de cicatrizaçao. Estudos mais especificos devem ser conduzidos para indicar o cimento Portland para uso clìnico, sendo que o MTA ja e de uso rotineiro em Endodontia. Palavras-chave: Cimento Portland; Agregado triòxido mineral; Patologia bucal.

ABSTRACT

Objectives:To evaluate the response of rat subcutaneous tissue to MTA, Portland cement and White Portland cement plus epoxy resin. Due to similarities in composition of MTA and Portland cement, white Portland cement was mixed with epoxy resin in order to obtain a more consistent material which would be easier to work with during clinical procedures. Methodology: MTA Angelus and Type II Portland Cement were mixed with distilled water in a 3:1 powder-liquid proportion. White Portland cement was mixed with epoxy-resin in the same proportion. The materials were placed into polyethylene tubes and implanted on the back of 36 Wistar rats. Implants of empty tubes were used as control. Animals were kiled at 7,30, and 60 days after implantation, and samples of the skin containing the tubes were removed and histologically processed. Results: At 7 days, a granulomatous tissue was observed nearby the extremity of the tube, characterized by lymphocytes, multinucleated giant cells, and abundant macrophages around a necrotic area. At 30 days, the tissue around the tube presented initial signs of repair characterized by fibrocytes and collagen fibers. A chronic inflammatory infiltrate characterized by many macrophages and some lymphocytes was also detected. At 60 days, an advanced process of repair was observed. No statistical differences were observed among the groups at 7 and 60 days (p>0,05); However some differences were seen at 30 days. More necrotic areas with granulomatous tissue and fibrosis were observed in Portland cement group when compared to the other cements (p<0,05). Lymphocytes were seen in much larger numbers in White Portland cement + epoxi resin group (p<0,05) (Kruskal-Wallis). Conclusions: The materials were not irritant to the tissues in the area, noticeably in the last periods, and did not interfere with the natural process of healing. Further studies are necessary to indicate Portland cement for clinical use, whereas MTA is already a routinely used product in endodontics. Keywords: Portland cement; Mineral trioxide aggregate; Oral pathology.

| Volver |