| O objetivo desta pesquisa foi avallar, in vitro, a influencia do tipo de adesivo na resistencia de uniáo de "brackets" metálicos colados ao
esmalte de dentes humanos. Trinta molares humanos extraídos foram incluidos em tubos de PVC e aleatoriamente divididos em tres grupos (n=10): Grupo I - "bracket" colado
com Transbond (3M/Unitek), Grupo II - "bracket" colado com AdheSE (Ivoclar/Vivadent) e Grupo III - "bracket" colado com Xeno III (Dentsply). O preparo da superficie de
esmalte foi realizada profilaxia, seguido da aplicacao dos adhesivos conforme instrucoes dos fabricantes. Os "brackets" metálicos (Morelli®) foram colados na porcao
central de cada fragmento com resina fotoativada Transbond XT (3M/Unitek). Os corpos-de-prova foram armazenados em agua destilada a 37°C durante 24 horas. Em seguida, foram
submetidos ao teste de cisalhamento em máquina de ensaio universal (EMIC, DL 2000), com velocidade de 1 mm/minuto e ao índice de Adesivo Remanescente (IAR). A análise estatística
(ANOVA/Tukey) demonstrou que o fator adesivo nao influencia a resistencia de uniáo ao cisalhamento. Dessa forma, os adesivos autocondicionantes sao uma boa alternativa
para a colagem de "brackets" metálicos. PALAVRAS-CHAVE: Adesivos autocondicionantes. Resistencia ao cisalhamento. Condicionamento Acido |
|
| Abstract | |
| The aim of this in vitro study was evaluate the influence of the adhesive type in the shear bond strength of metallics brackets to the dental enamel. Thirty
molars human were placed into PVC rings and randomly divided into three groups (n= 10). Group I - bracket bonded with Transbond (3M/Unitek), Group II - bracket bonded
with AdheSE (Ivoclar/Vivadent) and Group III - bracket bonded with Xeno III (Dentsply). The enamel surface was subjected to prophylaxis, followed by application of the
adhesive systems, according to the manufacturer's recommendations. The metallic brackets (Morelli®) were bonded in the central portion of the fragments with light-cure
resin Transbond XT (3M/Unitek). The specimens were stored in distilled water at 37°C for 24 hours. The samples were then submitted to shear bond strength in a universal
testing machine EMIC DL2000 at a cross-head speed of 1 mm/minute and index of Remainder Adhesive (ARI). The statistical analyses (ANOVA/ Tukey) showed the adhesive
system didn't influence the shear bond strength. In that way, the self-etching primers are a good alternative for the metallic brackets bonding. KEYWORDS: Self-etching adhesives. Shear bond strength. Acid conditioned. |
|
|