| REVISTA DA FACULDADE DE ODONTOLOGIA | |
| Vol. 47 No. 3 DEZEMBRO 2006 | |
| ISSN: 0566-1854 UBIC: 288-H | |
| Resumo | |
| Este trabalho estudou os efeitos da irradiacao iónica sobre as propriedades mecánicas de tres cerámicas odontológicas: Omega 900, Vitadur Alpha
e IPS Empress 2. Em urna primeira etapa, foi investigada a qualidade do acabamento superficial das cerámicas. Os melhores resultados foram obtidos com polimento tipo
metalográfico. Em urna segunda etapa, amostras das cerámicas, em forma de discos com pulimento metalográfico, foram irradiadas com íons de N de 500 keV e fluencia de
2 X 1016 íons/cm . Ensaios de friccao e desgaste tipo pino-sobre-disco entre discos cerámicos (virgens e irradiados) contra pinos de esmalte dental, foram realizados.
Foram também investigados a dureza e o módulo de Young das amostras cerámicas virgens e irradiadas através da técnica de nanoindentacáo. Os resultados obtidos mostraram
que a irradiacao iónica das amostras resultou em: i) reducSo do coeficiente de friccao e do desgaste entre os pares formados por cerámica irradiada e esmalte dental
(40%); ii) reducao da dureza (45%) e do módulo de Young (35%) na regiao irradiada das amostras. Estes resultados mostram que a irradiacao iónica pode ser usada para
modificar as propriedades mecánicas de cerámicas odontológicas comerciáis, transformando-as em materiais mais compatíveis com o esmalte dental. PALAVRAS-CHAVE: Cerámicas odontológicas. Acabamento superficial. Irradiacao iónica. Friccao. Desgaste. Dureza. |
|
| Abstract | |
| In this work were studied the ion irradiation effects on the mechanical properties of three dental ceramics: Omega 900, Vitadur Alpha e IPS Empress 2.
Initially, it was investigated the quality of surface finishing for the three ceramics. The best results were obtained using metallographic polishing. In a second phase
metallographicaly polished samples in form of small discs, were irradiated with 500 keV N ions at a fluence of 2 X 1016 íons/cm2. The friction coefficients and wear between
virgin and ion irradiated ceramics samples against enamel dental pins, were measured using a pin-on-disk tribometer. Hardness and Young modulus of the ceramic discs (virgin
and irradiated) have been also determined using the nanoindentation technique. The obtained results show that the ion irradiation produces: i)a reduction of 40% in
the friction coefficients and wear between the irradiated ceramic discs and the dental enamel, and ii) a decrease of hardness (45%) and Young modulus (35%) in the
irradiated region of the samples. There results show that ion irradiation can be used to modify the commercial dental ceramics mechanical properties, transforming them
into materials more compatible with dental enamel. KEYWORDS: Wear. Hardness. Dental ceramics. Superficial polishing. Ion irradiation. Friction. |
|
|